Sökning: "deformationer"

Visar resultat 1 - 5 av 32 avhandlingar innehållade ordet deformationer.

  1. 1. Behaviour of fracture process zones in concrete influenced by simultaneously applied normal and shear displacements

    Detta är en avhandling från Division of Building Materials, LTH, Lund University

    Författare :Manouchehr Hassanzadeh; Lunds universitet.; Lund University.; [1992]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; softening; mixed mode; fictitious crack model; concrete; deformationer; betong; brottmekanik; hållfasthet; brotthållfasthet; spänningar; skjuvspänningar; sprickor; beräkningsmodeller; brottenergi; teori; laboratorieförsök; interlock; crack path; diagonal crack; microcracking; instability; fracture energy; fracture mechanics; shear; tension; process zone;

    Sammanfattning : The thesis deals with the determination of the post peak behaviour of concrete in pure tension, and combined tension (compression) and shear. A test arrangement has been developed in order to determine the post peak behaviour of concrete expressed as stress - displacement curves. LÄS MER

  2. 2. Modelling of transport processes involved in service life prediction of concrete: important principles

    Detta är en avhandling från Division of Building Materials, LTH, Lund University

    Författare :Björn Johannesson; Lunds universitet.; Lund University.; [1998]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Byggteknik; Civil engineering; teori; beräkningsmodeller; finita element; beständighet; betong; livslängd; nedbrytning; sprickor; deformationer; hållfasthet; korrosion; klorider; fukt; simulering; luftporer; adsorption; beräkningsmetoder; desorption;

    Sammanfattning : The main focus in this licentiate thesis is a description of the environmentally introduced action of diffusing and chemically reactive (e.g. carbonation and chemical-physical adsorption-desorption) matter in the pore solution and in the air-filled space in the pore system of the material. LÄS MER

  3. 3. Time-dependent crack growth and fracture in concrete

    Detta är en avhandling från Division of Building Materials, LTH, Lund University

    Författare :Fan Ping Zhou; [1992]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; creep; rupture test; sustained loading; deformationer; betong; brottmekanik; sprickor; sprickbildning; sprickmodeller; krypning; spänningar; brottenergi; brottspänningar; beräkningsmodeller; finita element; teori; laboratorieförsök; creep rupture; tidsberoende; fracture mechanics; Fictitius Crack Model; finite element method; visco-elastic fracture; time-dependent fracture; creep crack growth; concrete; tensile fracture; crack model;

    Sammanfattning : The objectives of this thesis are to study time-dependent fracture behaviour in concrete. The thesis consists of an experimental study, constitutive modelling and numerical analysis... LÄS MER

  4. 4. Frysning av jord och berg vid tunnelbyggande. Studier av deformationer och spänningar

    Detta är en avhandling från Stockholm : KTH

    Författare :Teddy Johansson; KTH.; [2005]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TECHNOLOGY Civil engineering and architecture Building engineering; TEKNIKVETENSKAP Samhällsbyggnadsteknik och arkitektur Byggnadsteknik;

    Sammanfattning : .... LÄS MER

  5. 5. Stiffness of reverse channel connections at room and elevated temperatures

    Detta är en avhandling från Luleå : Luleå tekniska universitet

    Författare :Tim Heistermann; Luleå tekniska universitet.; [2013]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Steel Structures; Stålbyggnad;

    Sammanfattning : A frame structure exposed to fire undergoes two types of changes due to the resulting temperature fields. The first is the thermal expansion of the structural members and the second is the degradation of the material strength and stiffness as temperature rises. LÄS MER