Sökning: "Stress corrosion cracking"

Visar resultat 1 - 5 av 26 avhandlingar innehållade orden Stress corrosion cracking.

  1. 1. High temperature corrosion in a biomass-fired power boiler : Reducing furnace wall corrosion in a waste wood-fired power plant with advanced steam data

    Författare :Yousef Alipour; Pamela Henderson; Peter Szalalos; Christofer Leygraf; Jan Froitzheim; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; High temperature corrosion; Waterwalls; Power plant corrosion; NOx reducing enviroments; Biomass; Waste wood; Thermodynamic calculation modelling; corrosion-resistance alloy; Furnace wall corrosion; Högtemperaturekorrosion; Eldstadsväggar; kraftverks korrosion; låg Nox mijöer; biomassa; returträ; Termodynamisk modellering; korrosionsbeständighet legering; eldstadskorrosion;

    Sammanfattning : The use of waste (or recycled) wood as a fuel in heat and power stations is becoming more widespread in Sweden (and Europe), because it is CO2 neutral with a lower cost than forest fuel. However, it is a heterogeneous fuel with a high amount of chlorine, alkali and heavy metals which causes more corrosion than fossil fuels or forest fuel. LÄS MER

  3. 2. Corrosion testing of heat exchanger tubing

    Författare :Ulf Kivisäkk; KTH; []
    Nyckelord :corrosion testing; heat exchanger; stainless steels; general corrosion; immersion testing; activation; stress corrosion cracking; constant load; u-bends; relaxation; dewpoint corrosion;

    Sammanfattning : Heat exchanger tubes are commonly made from stainless steel.In a heat exchanger both the process fluid and the cooling orheating media can be corrosive. It is therefore important to beable to select materials that do not suffer from corrosion.Current methods in this area, however, suffer from limitationsand shortcomings. LÄS MER

  4. 3. Influence of hydrogen on corrosion and stress induced cracking of stainless steel

    Författare :Ulf Kivisäkk; Christofer Leygraf; Roy Johnsen; KTH; []
    Nyckelord :NATURVETENSKAP; NATURAL SCIENCES; hydrogen; corrosion; hydrogen embrittlement; stainless steels; uniform corrosion; activation; dewpoint corrosion; low temperature creep; plastic deformation; microhardness; Surface and colloid chemistry; Yt- och kolloidkemi;

    Sammanfattning : Hydrogen is the smallest element in the periodical table. It has been shown in several studies that hydrogen has a large influence on the corrosion and cracking behaviour of stainless steels. Hydrogen is involved in several of the most common cathode reactions during corrosion and can also cause embrittlement in many stainless steels. LÄS MER

  5. 4. Strain-assisted corrosion cracking and growth rate inhibitors

    Författare :Andrey P Jivkov; Mekanik; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; vacuum technology; vibration and acoustic engineering; Maskinteknik; hydraulik; vakuumteknik; vibrationer; akustik; materialteknik; Mechanical engineering; Material technology; Materiallära; Stress intensity factor; Inhomogeneous materials; Crack evolution; Stress corrosion cracking; Moving boundary; hydraulics;

    Sammanfattning : A model for evolution of cracks as a result of strain-assisted corrosion is presented. The considered cracks possess a realistic geometry, where the tip region is an integral part of the crack surface instead of being a singular point. This geometry is either implicitly defined or is a consequence of crack nucleation from surface irregularities. LÄS MER

  7. 5. On initiation of chemically assisted crack growth and crack propagation paths of branching cracks in polycarbonate

    Författare :Ulf Hejman; Malmö högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; stress corrosion; crack initiation; multiple cracking; polycarbonate; three point bending; stress corrosion cracking; polycarbonate; dissolution; branching; experiment; finite element modelling; stress corrosion; crack initiation; multiple cracking; polycarbonate; three point bending; branching.;

    Sammanfattning : Stress corrosion, SC, in some cases gives rise to stress corrosion cracking, SCC, which differs from purely stress intensity driven cracks in many aspects. They initiate and grow under the influence of an aggressive environment in a stressed substrate. They grow at low load and may branch. LÄS MER