Dissimilar joining of aluminium to ultra-high strength steels by friction stir welding

Sammanfattning: Multi-material structures are increasingly used in vehicle bodies to reduce weight of cars. The use of these lightweight structures is driven by requirements to improve fuel economy and reduce CO2 emissions. The automotive industry has replaced conventional steel components by lighter metals such as aluminium alloy. This is done together with cutting weight of structures using more advanced strength steels. However, sound joining is still difficult to achieve due to differences in chemical and thermal properties. This research aims to develop a new innovative welding technique for joining aluminium alloy to ultra-high strength steels. The technique is based on friction stir welding process while the non-consumable tool is made of an ordinary tool steel. Welding was done by penetrating the rotating tool from the aluminium side without penetrating into the steel surface. One grade of Al-Mg aluminium alloy was welded to ultra-high strength steels under lap joint configuration. Different types of steel surface coatings including uncoated, hot-dipped galvanised and electrogalvanised coating have been studied in order to investigate the influence of zinc on the joint properties. The correlation among welding parameters, microstructures, intermetallic formation and mechanical properties are demonstrated in this thesis.  Results have shown that friction stir welding can deliver fully strong joints between aluminium alloy and ultra-high strength steels. Two intermetallic phases, Al5Fe2 and Al13Fe4, were formed at the interface of Al to Fe regardless of surface coating conditions. The presence of zinc can improve joint strength especially at low heat input welding due to an increased atomic bonding at Al-Fe interface. The formation of intermetallic phases as well as their characteristics has been demonstrated in this thesis. The proposed welding mechanisms are given based on metallography investigations and related literature.