Image-based quantitative infrared analysis and microparticle characterisation for pulp and paper applications

Sammanfattning: Measurements of process variations and particle morphology are widely employed in the pulp and paper industry. Two techniques with high potential, infrared thermography and microparticle characterisation, are mainly used qualitatively. Quantitative thermography requires knowledge of the emittance, a material property which has not been measured under many process-relevant conditions. Quantitative characterisation of microparticles, e.g. pulp fines and mineral fillers, requires the analysis of a large number of particles, which can be accomplished using flow microscopes. Flow microscopes for pulp analysis have had insufficient spatial resolution to resolve fines and fillers. Additionally, there has been a lack of methods which can differentiate between fines and fillers in a mixed suspension.State-of-the-art instruments for particle image analysis were evaluated and compared to laser diffractometry, a measurement method based on scattering by diffraction. Laser diffractometry was found to be highly sensitive to the complex refractive index of the particles, and especially to its change due to moisture absorption. A high-resolution imaging flow cytometer and a high-resolution fibre analyser were found to be complementary for characterisation of pure fines and fines/filler mixtures, and superior to laser diffractometry. A method for differentiating between fines and fillers in a suspension based on their autofluorescence and side-scattering was proposed and qualitatively evaluated.Furthermore, a method for measuring the directional and integrated emittance of paper was developed and its accuracy was determined. Measurements on a wide range of samples showed that the emittance of fibre-based materials vary significantly with wavelength, pulp type, observation angle, and moisture content. By applying measured quantitative values of the emittance, the thermal energy emitted by sack paper samples during mechanical deformation could be quantitatively calculated. The increase in thermal energy at the time of rupture was found to correlate well with the elastic share of the mechanical energy that was stored in the sample during its elongation.In summary, the results of this work have facilitated the use of quantitative microparticle analysis and infrared thermography for pulp and paper applications.